Flat Platinum Electrode

Connecting cable PLUS with banana plug:     Color RED  Length 1,50 meter For connection directly to the device      Color RED Length 1.50 meters For connection directly to the device incl. a stainless steel crocodile clip.     4mm banana plugs molded on both sides with strain relief and bend protection. Re-connectable - any number of plugs can be plugged into each other. Cylindrical contact spring for large area contact in the socket. Nickel-plated contact surface for permanently low contact resistance. Fine stranded wire for highest flexibility and to avoid cable breakage. Conductor cross-section 1mm² - suitable for currents up to 25A. Double insulated cable with wear indicator by inner insulation in white -thereby damages at the insulation are immediately recognizable.   Pay attention to good quality for your electroplating and laboratory equipment! These cables have everything that is important for pleasant and durable use: large cross-section, good strain relief, gold-plated contacts and a flexible, yet resistant cable material with double insulation.  

Large XL Anode Pad – Replacement Pad for Flat Electroplating Electrodes (6 × 12 cm)Professional XL Anode Pad for Pen Plating and Brush Plating ApplicationsThe Large XL Anode Pad is a high-quality replacement pad specifically designed for professional pen plating and brush plating applications. It provides excellent electrolyte absorption and controlled electrolyte release, ensuring uniform current distribution and consistent metal deposition.With its generous dimensions of 6 × 12 cm, this XL anode pad is ideal for plating larger and flat surfaces efficiently. It is designed for use with flat platinum and stainless steel electrodes, making it the perfect accessory for decorative and technical electroplating applications.ApplicationsThe Large XL Anode Pad is ideal for:Pen platingBrush platingSelective electroplatingGold platingSilver platingRhodium platingPalladium platingPlatinum platingCopper platingNickel platingTin platingSurface restorationJewelry finishingWatch componentsIndustrial surface finishingRepair platingLarge flat workpiecesProduct BenefitsHigh-quality XL replacement anode padExcellent electrolyte absorptionEven electrolyte distributionUniform current transferSmooth and streak-free plating resultsSuitable for large and flat surfacesDurable and reusableEasy to replaceEasy to clean after useProfessional quality for demanding electroplating applicationsCompatibilityCompatible with:Flat platinum electrodesFlat stainless steel electrodesXL pen plating electrodesXL brush plating electrodesTechnical SpecificationsProduct TypeXL Replacement Anode PadDimensions6 × 12 cmMaterialHigh-performance electrolyte absorbent fabricReusableYesOptimized Electrolyte DistributionThe anode pad acts as an electrolyte carrier, providing an even transfer of electrolyte and electrical current to the workpiece surface. This results in uniform metal deposition, improved coating quality, and consistent plating performance.Its highly absorbent material stores sufficient electrolyte and releases it evenly during operation, helping to reduce streaking while improving coating quality and process reliability.Care InstructionsAfter each use, rinse the anode pad thoroughly with clean water to remove any remaining electrolyte residues. Allow it to dry completely before storage. With proper care, the pad can be reused many times while maintaining excellent performance.Delivery Includes1 × Large XL Anode PadSize: 6 × 12 cmQuality from Betzmann GalvanikBetzmann Galvanik develops professional accessories for pen plating, brush plating, and electroplating applications. Our anode pads are manufactured from high-quality materials to ensure optimum electrolyte distribution, long service life, and consistently reliable plating results.Whether used in jewelry manufacturing, watchmaking, industrial electroplating, restoration, or laboratory applications, Betzmann Galvanik accessories provide the quality professionals rely on.      

High-Speed Hard Gold Electrolyte 12 g/L – For Pen Plating, Tank Plating and Brush PlatingHigh-Speed Hard Gold for Fast, High-Quality Gold DepositsThe High-Speed Hard Gold Electrolyte containing 12 g/L gold is designed for electroplating applications requiring fast gold deposition. It is suitable for pen plating, tank plating and brush plating, allowing both precise local gold plating and the coating of suitable workpieces in a plating bath.According to the technical product specifications, the deposited gold layer has a gold content of 99.9% and a hardness of 220–230 HV. The specified deposition rate is approximately 0.8 µm per minute at 3.5 volts using a platinum electrode, under the stated reference conditions.With its high gold concentration and fast deposition rate, this electrolyte is suitable for demanding gold-plating work, decorative surface finishing and targeted replating applications.Key BenefitsHigh-Speed Hard Gold Electrolyte containing 12 g/L goldSuitable for pen plating, tank plating and brush platingGold content of the deposited layer: 99.9%Fast deposition rate of approximately 0.8 µm/min under the specified reference conditionsDeposit hardness of 220–230 HVSuitable for decorative gold plating and replatingFor use with platinum or carbon electrodesDesigned for professional users and demanding electroplating applicationsTechnical DataPropertySpecificationProduct typeHigh-Speed Hard Gold ElectrolyteGold concentration12 g/LVoltage range3.0–4.5 voltsOperating temperature14–25 °CElectrode materialPlatinum or carbonGold content of deposited layer99.9%Deposition rateApprox. 0.8 µm/min at 3.5 V with a platinum electrodeDeposit hardness220–230 HVDeposit density19.3 g/cm³Deposit stressMediumStorageProtect from sunlightShelf life1 yearPotassium cyanide content0.3%Transport classification according to product dataNot classified as dangerous goods for transport; no UN number specifiedPen Plating ApplicationsPen plating is particularly suitable for precise gold plating of small areas, edges, individual component sections and repair spots. Using a suitable plating unit and pen electrode, selected areas can be coated without immersing the entire workpiece in a plating bath.The specified voltage range is 3.0–4.5 volts. The appropriate setting depends on the plating unit, electrode, workpiece surface and operating conditions.Brush Plating ApplicationsIn brush plating, the electrolyte is applied to the prepared workpiece using a suitable applicator or swab saturated with electrolyte. This method is suitable for selective gold plating of larger areas and components that cannot be fully immersed in a plating bath.The stated deposition rate of approximately 0.8 µm per minute was calculated using a sample area that remains continuously covered by the plating swab. Actual deposition rates may vary depending on the application technique and operating conditions.Tank Plating ApplicationsTank plating is suitable for coating workpieces that can be fully or partially immersed in the electrolyte. It is particularly useful for components requiring coating over their accessible surfaces.Uniform results depend on suitable surface preparation, appropriate electrode positioning and process parameters adapted to the workpiece. The specified operating temperature is 14–25 °C.High-Speed Deposition and Hard Gold PropertiesThe specified deposition rate of approximately 0.8 µm per minute at 3.5 volts with a platinum electrode makes this electrolyte particularly suitable for applications where fast gold deposition is desirable.According to the product data, the deposited layer has a hardness of 220–230 HV and a gold content of 99.9%. The final coating properties and wear resistance also depend on surface preparation and plating conditions.Electrodes and Important Process NotesPlatinum or carbon electrodes are specified for this electrolyte. The use of stainless steel anodes is strongly discouraged for most plating processes.The stated deposition rate refers to a sample area that remains continuously covered by the plating swab. It should not automatically be applied to different surface geometries or assumed to be identical across all three plating methods.Storage and Shelf LifeStore the electrolyte protected from sunlight. The specified shelf life is 1 year.High-Speed Hard Gold from Betzmann GalvanikThe High-Speed Hard Gold Electrolyte 12 g/L is a versatile solution for pen plating, tank plating and brush plating. Its high gold concentration, specified fast deposition rate and deposit hardness make it an attractive choice for demanding gold-plating work and high-quality electroplated surface finishing.Betzmann Galvanik – Electroplating products and solutions for professional surface finishing.

Large Anode Pad 5 × 5 cm – Replacement Pad for Pen Plating and Brush PlatingProfessional Anode Pad for Precision Electroplating ApplicationsThe Large Anode Pad (5 × 5 cm) is a premium replacement pad designed for professional pen plating and brush plating applications. It has been specifically developed to provide excellent electrolyte absorption and controlled electrolyte release, ensuring uniform current transfer and consistent, high-quality metal deposition.With its practical 5 × 5 cm size, this anode pad is ideal for plating small to medium-sized workpieces as well as flat and slightly contoured surfaces. When used with flat platinum or stainless steel electrodes, it provides reliable current distribution and precise metal deposition for both decorative and technical electroplating applications.ApplicationsThe Large Anode Pad is ideal for:Pen platingBrush platingSelective electroplatingGold platingSilver platingRhodium platingPalladium platingPlatinum platingCopper platingNickel platingTin platingChromium platingJewelry finishingSurface restorationRepair platingTechnical surface finishingProduct BenefitsPremium replacement anode padExcellent electrolyte absorptionUniform electrolyte distributionSmooth and streak-free plating resultsConsistent current transferIdeal for small and medium-sized workpiecesDurable and reusableQuick and easy replacementEasy to clean after useProfessional quality for workshops, laboratories, and industrial electroplatingCompatibilityCompatible with:Flat platinum electrodesFlat stainless steel electrodesPen plating electrodesBrush plating electrodesTechnical SpecificationsProduct TypeReplacement Anode PadDimensions5 × 5 cmMaterialHigh-performance electrolyte-absorbing fabricReusableYesOptimized Electrolyte DistributionThe anode pad serves as an electrolyte carrier, ensuring even transfer of electrolyte and electrical current to the workpiece surface. This results in uniform metal deposition, consistent coating thickness, and an excellent surface finish.Its highly absorbent fabric retains sufficient electrolyte and releases it evenly throughout the plating process, helping to minimize streaking, reduce coating defects, and deliver reliable, repeatable electroplating results.Care InstructionsAfter each use, rinse the anode pad thoroughly with clean water to remove all electrolyte residues. Allow it to dry completely before storage. With proper care, the anode pad can be reused many times while maintaining excellent performance.Package Contents1 × Large Anode PadDimensions: 5 × 5 cmQuality from Betzmann GalvanikBetzmann Galvanik develops premium accessories for pen plating, brush plating, and electroplating applications. Our anode pads are manufactured from carefully selected materials to provide optimum electrolyte distribution, long service life, and consistent plating performance.Whether for jewelry manufacturing, watchmaking, restoration, industrial electroplating, or laboratory applications, Betzmann Galvanik accessories deliver the professional quality trusted by experts worldwide.

Hard Gold Electrolyte 8 g/L – For Pen Plating, Tank Plating and Brush PlatingHard Gold for High-Quality, Durable Gold CoatingsThis Hard Gold Electrolyte containing 8 g/L gold is designed for electroplating applications using pen plating, tank plating and brush plating. It allows precise local gold deposition as well as the coating of suitable workpieces in a plating bath.According to the technical product specifications, the deposited gold layer contains 99.9% gold and has a hardness of 220–230 HV. This makes the electrolyte particularly interesting for applications requiring an attractive gold finish combined with increased coating hardness.Whether you need decorative gold plating, replating of existing surfaces or targeted surface finishing of components, this electrolyte offers versatile applications for professional users and demanding DIY enthusiasts.Key BenefitsHard gold electrolyte with 8 g/L goldSuitable for pen plating, tank plating and brush platingGold content of the deposited layer: 99.9%Deposit hardness: 220–230 HVSuitable for decorative gold plating and replatingFor local coating applications and immersion platingApproximate deposition rate of 0.5 µm per minute under specified reference conditionsMaximum specified coating thickness: 5 µmTechnical DataPropertySpecificationProduct typeHard gold electrolyteGold concentration8 g/LVoltage range3–5 voltsOperating temperature14–25 °CElectrode materialPlatinum or carbonGold content of deposited layer99.9%Deposition rateApprox. 0.5 µm/min at 3.5 V with a platinum electrodeCathode efficiency35–40% at 3.5 V with a platinum electrodeMaximum coating thickness5 µmDeposit hardness220–230 HVDeposit density19.3 g/cm³Deposit stressMediumStorageProtect from sunlightShelf life1 yearPotassium cyanide content0.3%Transport classification according to product dataNot classified as dangerous goods for transport; no UN number specifiedPen Plating ApplicationsPen plating is particularly suitable for spot plating, small areas, edges and targeted repairs. Using a suitable plating unit and pen electrode, individual areas can be coated without immersing the entire workpiece in a plating bath.The specified voltage range is 3–5 volts. The appropriate setting depends on the plating unit, electrode, workpiece surface and operating conditions.Brush Plating ApplicationsIn brush plating, the electrolyte is applied to the prepared workpiece using a suitable applicator or swab saturated with electrolyte. This method allows selective gold plating of larger areas and complex components that cannot be fully immersed in a plating bath.The stated deposition rate of approximately 0.5 µm per minute refers to a test area that remains continuously covered by the plating swab. Actual deposition rates may vary with the surface area, application technique and operating conditions.Tank Plating ApplicationsTank plating is suitable for coating workpieces that can be fully or partially immersed in the electrolyte. It is particularly useful when an entire component or its accessible surfaces need to be plated.Uniform results require suitable surface preparation, appropriate electrode positioning and process parameters adapted to the workpiece. The specified operating temperature is 14–25 °C.Hard Gold with High Deposit HardnessThe specified deposit hardness of 220–230 HV is an important characteristic of this electrolyte. According to the product data, the deposited layer contains 99.9% gold.The term hard gold refers to the product characteristic stated in the manufacturer's specifications. Actual hardness and wear resistance also depend on plating conditions and the structure of the deposited layer.The maximum specified coating thickness is 5 µm. The actual deposition depends on factors such as plating time, power supply, electrode configuration and workpiece geometry.Electrodes and Process NotesPlatinum or carbon electrodes are specified for this electrolyte. Stainless steel anodes are expressly not recommended for most of the intended plating processes.The reference values for deposition rate and cathode efficiency apply at 3.5 volts using a platinum electrode. They should not automatically be applied to other electrode materials or assumed to apply identically to all three plating methods.Storage and Shelf LifeStore the electrolyte protected from direct sunlight. The specified shelf life is one year.Hard Gold Electrolyte from Betzmann GalvanikThe Hard Gold Electrolyte 8 g/L is a versatile solution for pen plating, tank plating and brush plating. The high gold content of the deposited layer and the specified hardness of 220–230 HV make it an interesting option for demanding gold-plating work, decorative surface finishing and targeted replating.Betzmann Galvanik – Electroplating products and solutions for high-quality surface finishing.