Gold Solution 4 Gramm /Liter
€37.00
Available, delivery time: 1-2 days
Product information "Gold Solution 4 Gramm /Liter"
Operating Conditions and Deposit Data
Plating Factor | 0.01 A/cm2 (see notes) |
Plating rate | 0.15 micron per minute at 0.01A/cm2, 20°C and low agitation ( see notes) |
Maximum plating thickness | 4 microns |
Temperature | 18 – 40 °C (see notes) |
pH | 4.3 – 4.5 |
Gold concentration | 4 grams per litre |
Turnovers to exhaustion | 20 – 24 grams of gold added per litre |
Agitation | Low to vigorous (see notes) |
Electrode | Mesh or Platinum Rod Electrode (preferably bagged) |
Gold content in plate | 99.9% (balance carbon) |
Cathode efficiency | ~25% at Plating Factor = 0.01A/cm2 |
Hardness | 190 – 210 Hv |
Density of deposit | 19.3 g/cm3 |
Stress | Medium |
Special storage requirements | Away from sunlight |
Shelf life | 1 – 2 years |
Health and Safety classification | Harmful |
Special considerations | Contains potassium cyanide (0.15%) |
Transport (UN number) | None: Not classified as dangerous for transport |
Notes:
- Recommended plating factor range is between 0.008 and 0.012 A/cm2
- The plating rate varies considerably with temperature and agitation at any
fixed plating factor. - The only gold that should be replenished is via Gold Tank Replenisher; the amount to add should be calculated using our online calculator.
- Evaporation losses are made up usually at the end of the day by topping back up to the original level with deionised water.
- Rinse articles above the solution when you remove them from the tank so all the gold solution left over on the work goes back into the tank and is not wasted. If not, the gold will be dragged out and wasted.
- One litre of gold solution should last between 5 and 6 turnovers. That means that a gold solution which has 4 grams per litre of gold in it as supplied should plate out at least 5 x 4 = 20 grams of gold before it becomes overloaded with potassium and starts to crystallise out as potassium salts.
Similar Items

Anode pad / tampon / anode sleeve / fuzzy sleeve / replacement fabric pad puffy from Betzmann Galvanik. This puffy fabric pad / anode sleeve or also called tampon is absolutely recommended for all plating processes. Optimally suitable for all coatings and electrolytes. The coating of larger areas is also quite fast with this pad. The insertion hole is larger than the electrode and therefore it happens that the moist anode pad slips off. Therefore, fix the pad on the electrode with a small rubber band.

Product information "Gold Flash" from Betzmann Galvanik Gold Flash with 2 grams of gold per liter - wonderfully suitable as an intermediate layer or decorative layer. The Gold Flash from Betzmann Galvanik has 2 main areas of application: 1. optical-decorative layer: Gold is soft and needs the addition of cobalt as a hard abrasion resistant top layer, which is not included in this product. Therefore, the gold layer from Goldflash appears somewhat lighter yellow. Parts that are not subject to any stress, such as souvenirs, horseshoes for decoration, etc., can be easily, directly and inexpensively gold-plated with the Goldflash. Tip: You can first gild parts very intensively and thickly with the Goldflash and then coat them briefly with the 8 or 12 gram cobalt-displaced hard gold! 2. bonding primer for the following coatings: Many applications require thin layers of gold before actual plating. Until now, this was only possible with the use of 24 carat gold and was therefore quite costly. cost-intensive. This is now a thing of the past. With the Goldflash from Betzmann Galvanik, you can now apply the desired gold layer. As an example, direct silver plating of nickel is usually not feasible, so you can first gold plate with the Goldflash, then silver plate. Likewise, when using black chrome, rose gold plating, green gold plating, the gold flash serves as an optimal bonding base when copper or nickel cannot be applied directly! Also, gilding nickel, which naturally oxidizes, is very easy and spotless. Then chrome plating on Goldflash can be done even easier and without problems. Despite gold plating, the material input is far below 10 cents per cm2 of surface! Recommended electrode: platinum electrode, graphite electrode Voltage: from approx. 4 volts Procedure: Polishing if necessary Degreasing Activate Goldflash Continue with the top layer chrome, white gold, rose gold, green gold Feature Used for Allows electroplating of a thin layer of strongly adherent gold. Before applying another layer of plating, for example when silver or palladium plating on stainless steel, nickel and its alloys. 24 carat thin coats of gold: electronics, optics – reflectors – and where the item is going to be protected with a clear lacquer layer. Operating Conditions and Deposit Data Voltage Range 4.0 – 6.0 volts Temperature 14 – 25 °C Gold Concentration 2g/l Electrode Platinum or Carbon (see notes) Gold content in plate 99.9% (balance carbon) Plating Rate at (5.0 volts, Platinum electrode) Approx. 0.12 micron per minute (spot) Hardness 180 – 190 Hv Density of deposit 19.0 g/cm3 Stress Low – medium stress Special storage requirements Away from sunlight Shelf life Over 3 years Notes: We strongly advise against the use of stainless steel anodes for most of our plating processes Plating rates are calculated over a sample area which is permanently covered by swab. Features Used for Designed mainly as a base solution for mixing with our Coloured Gold Mixers Mixing with Yellow, White, Rose, and Green Gold Mixers and Brass Effect Gold Mixer. Can be mixed with 2 or more Gold Mixers Creating a huge spectrum of different shades and tints of gold – good for exactly matching colour of original gold plated layer Can be plated on its own, forming a soft, 24 carat gold layer, completely cyanide free Mainly functional purposes only. Needs a Gold Flash undercoat if plating on to stainless steel Signalword : Warning H-phrases: H332 Harmful by inhalation. H312 Harmful in contact with skin. H302 Harmful if swallowed. P phrases: P280 Wear protective gloves/protective clothing/eye protection/face protection. P301 IF INFECTED:P310 Immediately call a POISON CENTER/doctor/
Content: 0.05 Liter (€640.00 / 1 Liter)

PRODUCT PRESENTATION - HIGH SPEED GOLD ELEKTRTOLYT 999 FINE GOLD - 23,8 CARAT WITH 12 GRAMS OF GOLD PER LITER More gold in the electrolyte means even faster plating, thicker layers with the same working time or more surface area. Also the purchase of the high speed gold is cheaper, because you buy more gold per liter at a lower price. Do-it-yourself gold plating has never been easier. Our gold electrolyte from Betzmann Galvanik can be purchased by anyone. So whether it is for use in the highly professional use of laboratories, industry, luxury companies, to the use in the hobby, main or in the side business, companies, schools, universities, TH , IHK or other authorities. With this extremely fast and very hard depositing gold electrolyte from Betzmann Galvanik, you can usually coat the following metals directly: Stainless steel of all kinds, surgical steel, copper, silver, brass, nickel, iron, steel, The pink color of the electrolyte is the hardness additive cobalt. This gives the otherwise much too soft gold an abrasion resistant surface. This is not toxic in the admixed composition. The gold electrolyte from Betzmann Galvanik is anti-allergenic, was extracted from crisis- and conflict-free gold and is food-safe. Our Betzmann Galvanik Gold Electrolyte has a very fast deposition and further achieves a very hard gold layer. It has a very good covering effect and is therefore one of the best products on the market worldwide. A special preservative results in a very long shelf life of at least 2 years and prevents sedimentation, which occurs with many other gold electrolytes. The Gold Electrolyte from Betzmann Galvanik can be used for pen electroplating, pad electroplating and also for bath electroplating! The Gold Electrolyte from Betzmann Galvanik is used worldwide, e.g. for the gold plating of boat parts made of brass that are exposed to salt water, medical technology, measurement technology, for optical gold plating, for technical gold plating, gold plating of drive shafts, musical instruments and their parts, both inside and outside, body jewelry, intimate protection, dental jewelry, dental technology, drills of all kinds, shisa, e-cigarettes so-called. Vaporizers, vehicle parts, engine parts, motorcycle parts, airplane interiors, exhaust systems and manifolds, as gold is very heat resistant, sporting goods, diving equipment, keys and pendants, jewelry, chains and rings of all kinds, piston rods, pipes, table feet, bathroom fixtures and many more. Partial coatings are possible by masking and masking surrounding areas. To avoid material loss when coating sloping surfaces, we recommend our thickener/gel former. With this you can thicken all electrolytes also chrome remover, cleaner etc.. Also you can use with this gold mostly in the ratio 1:10 our mixer products like rose gold, white gold and green gold! Optimal results are achieved with the platinum electrode 6mm - 10cm long or the flat platinum electrode, since platinum electrodes can build up very thick layers far above 10 microns and more. Graphite electrodes can also be used. Gold content: 12 grams per liter The procedure for gold plating: It is recommended to polish the surface to a shine first - the nicer the surface, the nicer the shine will be Thorough degreasing with the electrocleaner Activate the surface with the activator Gilding with platinum electrode starting around 5 volts Operating Conditions and Deposit DataVoltage Range3.0 – 4.5 voltsTemperature14 – 25 °CGold Concentration12g/lElectrodePlatinum or Carbon (see notes)Gold content in plate99.9% (balance carbon)Plating Rate at (3.5 volts, Platinum electrode)Approx. 0.8 micron per minute (spot)Hardness220 – 230 HvDensity of deposit19.3 g/cm3StressMedium stressSpecial storage requirementsAway from sunlightShelf life3 – 6 monthsHealth and Safety classificationHarmfulSpecial considerationsContains potassium cyanide (0.3%)Transport (UN number)None: Not classified as dangerous for transport Notes:We strongly advise against the use of stainless steel anodes for most of our plating processesPlating rates are calculated over a sample area which is permanently covered by swab.
Content: 0.05 Liter (€1,880.00 / 1 Liter)

Platinum electrode from Betzmann-Galvanik: We know that when plating with gold or silver, you want to achieve only the best results and this is achieved by using our platinum electrode (platinized titanium). This will more than meet your requirements. It hardly wears out and leaves no black spots or stains when plating. For top quality gold plating, we recommend the use of this electrode. Care should be taken to clean the electrode carefully after each use! Properties "Platinum Electrode 6 mm Platinum electrode (platinized titanium with a platinum layer of 2.5 µm platinum) Ø 6 mm x 100 mm Standard electrode for experiments in electrochemistry (electroplating, electrolysis, ion migration, determination of electrochemical potentials, etc.) Spare platinum electrode for Hofmann decomposition apparatus, electrolyzer Platinum-coated titanium anodes are among the classic anode materials for electroplating because they combine the excellent electrochemical properties of platinum with the good corrosion properties of titanium. They are characterized by a long service life at high current density and are versatile in use. They are equally suitable for platinum and ruthenium baths, for hard chrome plating, as bright rhodium baths and for cathodic corrosion protection. The standard platinum layer thickness is 2.5 μm. In order to achieve the best results when plating with gold (adhesive gold bath, bright gold plating bath) or silver, they are indispensable. This platinum electrode will more than meet your requirements, it hardly wears out and leaves no black spots or stains when plating. For top quality gold plating, I recommend using this electrode. Other possible applications: Water electrolysis/separation of hydrogen and oxygen, water disinfection, production of chlorates (chlorate synthesis) and perchlorates. Recommended operating data: Operating voltage from 3 volts distance anode/workpiece surface 5 cm anodic current intensity (specific current density) max. 75 A/dm² (7.5 mA/mm² = 750 mA/cm²), i.e. a multiple of the values typical in electroplating (0.5 ... 5 A/dm²) pH value: 0 - 11 Bath temperature max. 60 °C

PRODUCT PRESENTATION - GOLD ELECTRTOLYT 999 FINE GOLD - 23,8 CARAT WITH 8 GRAMS OF GOLD PER LITER Do-it-yourself gold plating has never been so easy. Our gold electrolyte from Betzmann Galvanik may be purchased by anyone. Whether it is for use in highly professional laboratories, industry, luxury companies, to the use in the hobby, main or secondary trade, companies, schools, universities, TH , IHK or other authorities. With this extremely fast and very hard depositing gold electrolyte from Betzmann Galvanik, you can usually coat the following metals directly: Stainless steel of all kinds, surgical steel, copper, silver, brass, nickel, iron, steel, The pink color of the electrolyte is the hardness additive cobalt. This gives the otherwise much too soft gold an abrasion resistant surface. This is not toxic in the admixed composition. The gold electrolyte from Betzmann Galvanik is anti-allergenic, was extracted from crisis- and conflict-free gold and is food-safe. Our Betzmann Galvanik Gold Electrolyte has a very fast deposition and further achieves a very hard gold layer. It has a very good covering effect and is therefore one of the best products on the market worldwide. A special preservative causes a very long shelf life of at least 2 years and prevents sedimentation, as it occurs with many other gold electrolytes. The gold electrolyte from Betzmann Galvanik is used worldwide, e.g. for the gold plating of boat parts made of brass that are exposed to salt water, medical technology, measurement technology, for optical gold plating, for technical gold plating, gold plating of drive shafts, musical instruments and their parts, both inside and outside, body jewelry, intimate protection, dental jewelry, dental technology, drills of all kinds, shisa, e-cigarettes so-called. Vaporizers, vehicle parts, engine parts, motorcycle parts, airplane interiors, exhaust systems and manifolds, as gold is very heat resistant, sporting goods, diving equipment, keys and pendants, jewelry, chains and rings of all kinds, piston rods, pipes, table feet, bathroom fixtures and many more. Partial coatings are possible by masking and masking surrounding areas. To avoid material loss when coating sloping surfaces, we recommend our thickener/gel former. With this you can thicken all electrolytes also chrome remover, cleaner etc.. Also you can use with this gold mostly in the ratio 1:10 our mixer products like rose gold, white gold and green gold! Optimal results are achieved with the platinum electrode 6mm - 10cm length or the flat platinum electrode, because platinum electrodes can build up very thick layers far over 10 microns and more. Graphite electrodes can also be used. Gold content: 8 grams per liter The procedure for gilding: Recommended to first polish the surface to a shine - the nicer the surface, the nicer the shine will be Thorough degreasing with the electrocleaner Activate the surface with the activator Gilding with platinum electrode starting around 5 volts Operating Conditions and Deposit DataVoltage range3 – 5 voltsTemperature14 – 25 °CGold concentration8 g/lElectrodePlatinum or Carbon (see notes)Gold content in plate99.9% (balance carbon)Plating rate at (3.5 volts, Platinum electrode)Approx. 0.5 micron per minute (spot)Cathode efficiency (3.5 volts, Platinum Electrode)35 – 40%Maximum plating thickness5 micronsHardness220 – 230 HvDensity of deposit19.3 g/cm3StressMedium stressSpecial storage requirementsAway from sunlightShelf life1 – 2 yearsHealth and Safety classificationHarmfulSpecial considerationsContains potassium cyanide (0.3%)Transport (UN number)None: Not classified as dangerous for transport
Content: 0.05 Liter (€1,570.00 / 1 Liter)

Covering pen for partial coating Betzmann Galvanotechnik: Use this concealer pen to cover areas that are not to be coated. Simply apply the liquid agent, let it dry and then you can coat. After the process, simply rub off like an eraser.
Content: 0.025 Liter (€640.00 / 1 Liter)