White Gold Mixer

White Palladium Electrolyte 10 g/L BMG‑101M High‑Performance Palladium Plating Solution for Bright, Silver‑White Coatings Short Description The White Palladium Electrolyte 10 g/L BMG‑101M is a premium electroplating solution designed to deposit bright, silver‑white palladium layers. With a palladium concentration of approximately 10 g per liter, this electrolyte produces a brilliant, metallic finish that is even more striking than traditional nickel plating. real-gold.de It can be used both as a hard decorative top layer and as a nickel‑free barrier layer in multi‑step plating systems. real-gold.de Applications White palladium plating is suitable for: Applying bright silver‑white palladium coatings Nickel‑free barrier layers between copper/brass and gold Decorative finishes with high corrosion resistance Prepping surfaces for subsequent gold plating Alternatives to silver plating, as palladium does not tarnish easily  This makes it especially useful for jewelry, electronics, and other applications where an elegant, durable, and nickel‑free surface is desired.  How White Palladium Plating Works (Simple Explanation) Palladium electroplating works by using direct current (DC) to reduce palladium ions from the electrolyte onto the surface of the workpiece: Surface Preparation: Clean and degrease the part thoroughly. Plating: Connect the workpiece as the cathode and apply appropriate voltage. Deposition: Palladium ions reduce and form a uniform, silver‑white metallic coating. Finishing: Rinse with water and dry after plating.  Benefits of White Palladium Electrolyte BMG‑101M Extremely bright, silver‑white metallic finish, brighter than traditional nickel coatings  Nickel‑free and allergen‑free, ideal for skin‑contact applications  Acts as an excellent barrier layer between base metals and gold  High corrosion resistance and very low porosity, improving durability  Suitable on many substrates, including copper, nickel, brass, silver, gold, and dechromed surfaces  Can be solder‑wetted and provides strong performance on electrical contacts Technical Parameters (Practical Data) PropertyValue / RangeElectrolyte typePalladium plating solutionPalladium contentapprox. 10 g/LRecommended voltage3.0–3.5 V (pin electroplating from ~3 V, bath 3–4 V)Operating temperature48–52 °CpH7.0–8.0Deposition rateapprox. 0.17 µm/min at 0.0075 A/cm²Hardnessapprox. 488 HVDensity of depositapprox. 11.85 g/cm³Deposit purity~99.9 % palladiumAnodePlatinum mesh or graphiteAgitationVery low (mini stir rod)Lightness (L*)65 (CIE L* value)Shelf life1–2 yearsHealth/Safety classificationIrritantTransport classificationNot classified as hazardous Note: These values are practical guidelines and may vary depending on equipment, voltage, and material.  Practical Application Instructions Surface Preparation: Clean and degrease parts thoroughly to remove oils and contaminants. Plating: Heat the solution to the recommended temperature (48–52 °C). Apply recommended voltage; stable agitation with a mini stir rod improves coating uniformity. Post‑Treatment: Rinse parts with clean water after plating. Dry carefully; light polishing can enhance the finish if desired. Safety Instructions White palladium electroplating solutions contain active chemical components and must be handled with care: Wear protective gloves, eye protection, and suitable clothing Avoid contact with skin and eyes Rinse thoroughly with water if contact occurs Operate in well‑ventilated areas Do not ingest; keep out of the reach of children Dispose of waste according to local chemical waste regulations  Conclusion The White Palladium Electrolyte 10 g/L BMG‑101M is a professional‑grade electroplating solution that delivers very bright, silver‑white palladium coatings with excellent durability and low porosity. It is particularly suitable for decorative and functional applications, and as a nickel‑free barrier layer before gold plating, making it ideal for jewelry, electronics, and precision metalwork

Mixer set for measuring Real Gold Betzmann  With this mixer set consisting of 1x measuring cylinder3x pipette3 x beaker you can mix rose gold, white gold, green gold, etc. in the right proportion exactly.

K-Gold Electroplating Solution – for Pen, Bath & Swab Plating (10 g) Professional cyanide-free gold electrolyte for selective and immersion plating The K-Gold electroplating solution is a premium, cyanide-free gold electrolyte designed for pen plating, swab (tampon) plating and bath electroplating. It is ideal for jewellery finishing, repair plating, precision components and controlled gold deposition on small parts. The solution deposits a high-purity gold layer (up to 24 K) with excellent adhesion and uniform thickness. It can be used pure or blended with coloured gold additives to achieve specific karat values and gold shades. 🔷 Key Features & Benefits High-purity gold electrolyte (≈ 10 g Au/L equivalent) Cyanide-free formulation for safer professional use Suitable for three plating methods: – Pen plating – Swab / tampon plating – Bath (immersion) plating Excellent adhesion on nickel, copper, silver and brass (proper pretreatment required) Soft, burnishable gold deposit with high visual quality ⚙️ Technical Parameters Gold concentration: approx. 10 g/L equivalent Deposit purity: 99.9–100 % gold Operating voltage: – Pen / swab plating: from 3.5 V – Bath plating:  3 V (current-controlled recommended) begin with 0,1 Ampere pro cm2 Temperature: 20–25 °C Recommended anode: Carbon or platinised titanium (bath) Hardness: approx. 170–180 HV Density: approx. 19.0 g/cm³ 🖊️ Pen Plating Application Ideal for localised plating, repairs and touch-ups. Clean, degrease and activate surface Load plating pen or swab with K-Gold solution Apply 2–3.5 V Move evenly across the surface to build the layer 🧽 Swab / Tampon Plating Application Best for controlled selective plating on larger areas. Soak swab with electrolyte Maintain gentle, even contact Keep voltage stable Repeat passes to achieve desired thickness 🧪 Bath Plating Application For uniform full-surface gold plating of small components. Thorough surface preparation Fill plating bath with K-Gold solution Use carbon or platinised titanium anode Apply low current density at 2–4 V Rinse and dry after plating ℹ️ Notes Air-sensitive – reseal container immediately after use Can be mixed with gold colour additives for karat matching Suitable for decorative and functional gold coatings

Gold Whitener BMG-122.3 – Mixing Solution for Adjusting Gold Shades Short Description: The Gold Whitener BMG-122.3 is a specially developed mixing solution used in electroplating to lighten gold colors or modify gold tones. When mixed with a standard gold electrolyte, it allows the creation of a wide range of shades – from classic 18-karat yellow gold to champagne or white-gold-like tones. What is the Gold Whitener? The Gold Whitener is an additive (mixer) that is combined with a regular gold electrolyte to adjust and brighten the color of the deposited gold layer. Depending on the mixing ratio, it can produce elegant 18-karat gold tones, lighter yellow gold, champagne shades, or even white-gold-like finishes. What is it used for? Adjusting gold colors: Create lighter or softer gold shades such as 18 K, 14 K, champagne, or white-gold-like tones. Flexible color control: The more Gold Whitener added, the lighter the resulting gold color. Compatible with standard gold electrolytes: No need for a separate base electrolyte – simply mix with your existing gold solution. Application & Mixing Ratio Standard mixture: Mix 2 ml Gold Whitener with 10 ml gold electrolyte to achieve a typical 18-karat gold tone. Lighter shades: Higher proportions of Gold Whitener result in lighter gold or champagne tones. Can also be used undiluted if required. Recommended electrodes: Platinum electrode – for fine, uniform, high-quality coatings Graphite electrode – versatile and widely used Properties & Technical Data Operating voltage: approx. 3.0 – 5.0 V Operating temperature: approx. 18 – 25 °C (room temperature) Gold concentration: approx. 8 – 4 g/l in the electrolyte Coating characteristics: Gold content of the deposit: from 99.9 % (yellow gold) down to approx. 75 % (light, white-gold-like shade) Deposition rate (at approx. 3.5 V with platinum electrode): approx. 0.5 µm per minute (spot plating) Hardness: approx. 220 Hv (yellow gold) to 550 Hv (white-gold-like) Density of the deposit: 15.0 – 19.0 g/cm³ Shelf life: More than 3 years under normal storage conditions Advantages & Applications Highly flexible: Enables a wide range of gold color variations using one base electrolyte Customer-specific finishes: Ideal for matching individual color requirements Cost-effective: No need to maintain multiple gold electrolytes Safety & Notes Not suitable for stainless steel electrode systems during electroplating processes (except for degreasing, activating, or dechroming). Always follow the safety instructions and product documentation provided. Conclusion The Gold Whitener BMG-122.3 is a versatile professional mixing solution for creating lighter gold shades, champagne tones, and white-gold-like finishes. By simply adjusting the mixing ratio with a standard gold electrolyte, you gain full control over the final gold color – from classic 18-karat yellow gold to very light, elegant tones.