Product information "Platinum Solution 2 G./Liter"

Platinum Electrolyte with 2 Gramm Platinum per Liter!

Platinum Bath - Platinizing with Betzmann Electroplating

Platinum is characterized by high abrasion resistance and gives a noble gray surface.

Alternative: White palladium

The platinum bath from Betzmann Galvanik deposits corrosion-resistant, very bright and shiny platinum layers up to a thickness of 0.5 - 1.0 µm.

It is suitable for both decorative and technical applications and is very well suited for pin, bath and pad electroplating!..

Operating data:

Platinum content: 2.0 g/L

pH-value: <1

Density: 1.08 g/ml, increasing

Working conditions:

Voltage: from 3 volts

Bath temperature: 30 - 40 °C

Exposure time: 2 - 4 min.

Anode material: platinized titanium

Anode/cathode surface: 1 : 1

Fabric movement: required

Recommended speed: 2 - 8 cm/sec.

Deposition rate: approx. 11 mg/Amin; approx. 0.5-1.5 A/dm2

Bath movement: recommended

Precipitation data:

Hardness: 500 HV

Layer thickness: max. 1.0 µm

Fineness: 99,9%

Delivery form:

Ready to use 2 g/L Pt

Features	Applications
High concentration of platinum – 2 grams per litre	Suitable for brush plating both decorative and functional items such as jewellery and electrical connectors

Operating Conditions and Deposit Data

Voltage Range	3.0 – 5.0 volts
Temperature	20 – 25 °C (25 °C preferred)
Platinum concentration	2 g/l
Electrode	Platinum - Carbon
Platinum content in plate	Above 99.9%
Plating Rate at (3.5 volts, Platinum electrode)	Approx. 0.25 micron per minute (spot) – see notes)
Hardness	405 Hv
Density of deposit	21.4 g/cm3
Electrical resistivity of deposit	9.8 micro ohms/cm
Stress	Not determined
Special storage requirements	None
Shelf life	Over 2 years
Health and Safety classification	Irritant
Special considerations	None
Transport (UN number)	2796

Notes:

We strongly advise against the use of stainless steel anodes for most of our plating processes.
Higer voltages give greater plating rates, however more gas is liberated and a mist mask is recommended.
Plating rates are calculated over a sample area which is permanently covered by swab.
Will plate directly onto freshly prepared nickel or stainless steel.

Hazard statements

betzmann-galvanik-solution

H314 Causes severe skin burns and eye damage.

Precautionary statements

P280 Wear protective gloves/protective clothing/eye protection/face protection.

P302 IN CASE OF CONTACT WITH SKIN:

P352 Wash with plenty of water.

P332 If skin irritation occurs:

P313 Get medical advice/attention.

P362 Take off contaminated clothing.

0 of 0 reviews

Leave a review!

Share your experiences with other customers.

Login

Your email address

Your password

No reviews found. Share your insights with others.

Similar Items

Anode sleeve fuzzy

Anode pad / tampon / anode sleeve / fuzzy sleeve / replacement fabric pad puffy from Betzmann Galvanik. This puffy fabric pad / anode sleeve or also called tampon is absolutely recommended for all plating processes. Optimally suitable for all coatings and electrolytes. The coating of larger areas is also quite fast with this pad. The insertion hole is larger than the electrode and therefore it happens that the moist anode pad slips off. Therefore, fix the pad on the electrode with a small rubber band.

€2.38*

Carbon Electrode 6mm

Graphite round rod - Graphite rod anode - Graphite electrode for gold plating. Graphite electrodes are ultimate for all coatings. The advantage is that in some coatings with stainless steel electrodes, the dislodged metal parts disturb the coating. This does not happen with graphite electrodes, because graphite also filters out contaminated liquids. With bath electroplating, they also need to be replaced occasionally as they slowly dissolve during the plating process. With pad electroplating, simply loosen the screw on the handle and replace with a new one. Diameter 6 mm, length approx. 9 cm Features Used for Doesn’t contaminate Cleaner Activating and electro-cleaning Its resistive properties help to heat the solution you’re plating with Chromium plating, which needs to be plated at 25 degrees celsius; its natural heating action helps to maintain the solution’s optimal temperature Low cost Can be used for all plating processes but carbon electrodes deteriorate over a period of time and discolour swabs (discolouration does not affect the plating quality)

€5.90*

Platinum Electrode

Platinum electrode from Betzmann-Galvanik: We know that when plating with gold or silver, you want to achieve only the best results and this is achieved by using our platinum electrode (platinized titanium). This will more than meet your requirements. It hardly wears out and leaves no black spots or stains when plating. For top quality gold plating, we recommend the use of this electrode. Care should be taken to clean the electrode carefully after each use! Properties "Platinum Electrode 6 mm Platinum electrode (platinized titanium with a platinum layer of 2.5 µm platinum) Ø 6 mm x 100 mm Standard electrode for experiments in electrochemistry (electroplating, electrolysis, ion migration, determination of electrochemical potentials, etc.) Spare platinum electrode for Hofmann decomposition apparatus, electrolyzer Platinum-coated titanium anodes are among the classic anode materials for electroplating because they combine the excellent electrochemical properties of platinum with the good corrosion properties of titanium. They are characterized by a long service life at high current density and are versatile in use. They are equally suitable for platinum and ruthenium baths, for hard chrome plating, as bright rhodium baths and for cathodic corrosion protection. The standard platinum layer thickness is 2.5 μm. In order to achieve the best results when plating with gold (adhesive gold bath, bright gold plating bath) or silver, they are indispensable. This platinum electrode will more than meet your requirements, it hardly wears out and leaves no black spots or stains when plating. For top quality gold plating, I recommend using this electrode. Other possible applications: Water electrolysis/separation of hydrogen and oxygen, water disinfection, production of chlorates (chlorate synthesis) and perchlorates. Recommended operating data: Operating voltage from 3 volts distance anode/workpiece surface 5 cm anodic current intensity (specific current density) max. 75 A/dm² (7.5 mA/mm² = 750 mA/cm²), i.e. a multiple of the values typical in electroplating (0.5 ... 5 A/dm²) pH value: 0 - 11 Bath temperature max. 60 °C

€49.00*