Alkaline Copper BMG 093M – Precision, Adhesion & Professional Results The Alkaline Copper from Betzmann Galvanik is a high-performance, versatile electroplating electrolyte designed for demanding applications in bath plating, pen plating, and tampon plating. Engineered for maximum adhesion and uniform deposition, this electrolyte produces smooth, low-stress copper layers, making it ideal as both an intermediate layer and a decorative finish. Suitable for both beginners and professionals, it ensures consistent and reliable results across a wide range of applications. Key Benefits at a Glance Excellent adhesion on various metals Smooth, dense and uniform copper layers Perfect for complex geometries and fine details Suitable for: Bath electroplating Pen plating Tampon plating Beginner-friendly yet professional-grade Reduced internal stress for crack-free coatings Applications Jewelry manufacturing & finishing Repair and restoration Model making & precision engineering PCB and technical applications Decorative metal finishing Technical Parameters Electrolyte type: Alkaline Metal: Copper Application methods: Bath, pen, and tampon plating Working temperature: approx. 20–30 °C pH value: Alkaline (stabilized) Current density: Bath: approx. 0.5 – 2.5 A/dm² Pen/Tampon: adjustable depending on use Voltage: approx. 1–6 V Anode material: Copper (recommended) Application Guide (Beginner to Professional) 1. Surface Preparation (critical for adhesion) Thoroughly degrease the workpiece Activate / pickle depending on base material Rinse with distilled water Avoid touching the surface afterwards 2. Bath Electroplating (efficient & uniform) Fully immerse the workpiece in the electrolyte Apply DC current (follow recommended current density) Plate until desired thickness is achieved Use agitation for uniform results Ideal for larger parts and batch processing 3. Pen Plating (precise & flexible) Apply electrolyte via felt or sponge tip Move the plating pen evenly across the surface Start with low voltage and increase gradually  Perfect for small areas, repairs and detail work  4. Tampon Plating (controlled & mobile) Soak tampon with electrolyte Apply directly to the surface Maintain even pressure and movement  Best for selective plating and hard-to-reach areas  Pro Tips for Best Results Lower current density = finer, smoother layers Higher current density = faster build-up (risk of roughness) Always work with clean solutions and tools Rinse between steps for better quality Maintain stable temperature Conclusion The Alkaline Copper BMG 093M is the perfect choice for anyone seeking reliable, high-quality and versatile copper plating results. Whether you're a beginner or a professional, this electrolyte delivers excellent adhesion, smooth finishes, and consistent performance.

White Bronze Electrolyte SW10011.1 Fast plating electrolyte for bright white bronze coatings as an alternative to nickel Short Description The White Bronze Electrolyte SW10011.1 is a brush or bath electroplating solution for depositing a bright white bronze alloy on conductive metal surfaces. When used, it produces an antimicrobial white bronze layer that can replace traditional nickel plating, replicating similar hardness and color while avoiding nickel allergy issues. Real Gold Applications This bronze plating electrolyte is used to: Apply bright white bronze coatings on a variety of metals Replace nickel plating where nickel avoidance is desired Provide corrosion-resistant and antimicrobial layers Act as a barrier layer between copper/brass and gold Create decorative or functional coatings in brush or bath plating Real Gold How It Works (Simple Explanation) White bronze plating is achieved by mixing this electrolyte with an alkaline copper plating solution (1:1) and applying direct current. The bronze alloy deposits as a uniform, bright metallic layer. Real Gold Benefits High deposition rates and efficient operation Nickel-free alternative with similar physical properties Antimicrobial and corrosion-resistant surface Functions as a barrier layer before gold plating Decorative and functional surface finish Compatible with brush and bath plating Real Gold Typical Parameters PropertyValue / RangeElectrolyte typeWhite bronze plating solutionMixing ratio1 part alkaline copper : 1 part White BronzeVoltage3.2–3.5 VTemperature18–25 °C (optimum ~22 °C)ElectrodeGraphite/platinumTypical alloy~42 % Cu / 58 % SnHardness450–500 HVDensity of deposit8.6–8.8 g/cm³Plating rate0.7–1.5 µm/minShelf life~4 weeks if stored correctlyStorage2–5 °C recommendedAir sensitiveYes — keep sealed Safety Information Follow all standard electroplating safety practices: Wear protective gloves, goggles, and clothing Avoid contact with skin and eyes Use in well-ventilated areas Keep out of reach of children Dispose of wastes per local regulations Conclusion The White Bronze Electrolyte SW10011.1 is a versatile plating solution that produces bright, antimicrobial white bronze coatings with mechanical and aesthetic properties close to nickel plating. It is especially useful where nickel use is restricted or undesirable, and as a barrier layer prior to gold plating in both decorative and functional applications.

White Bronze Electrolyte SW10011.1 Fast plating electrolyte for bright white bronze coatings as an alternative to nickel Short Description The White Bronze Electrolyte SW10011.1 is a brush or bath electroplating solution for depositing a bright white bronze alloy on conductive metal surfaces. When used, it produces an antimicrobial white bronze layer that can replace traditional nickel plating, replicating similar hardness and color while avoiding nickel allergy issues. Real Gold Applications This bronze plating electrolyte is used to: Apply bright white bronze coatings on a variety of metals Replace nickel plating where nickel avoidance is desired Provide corrosion-resistant and antimicrobial layers Act as a barrier layer between copper/brass and gold Create decorative or functional coatings in brush or bath plating Real Gold How It Works (Simple Explanation) White bronze plating is achieved by mixing this electrolyte with an alkaline copper plating solution (1:1) and applying direct current. The bronze alloy deposits as a uniform, bright metallic layer. Real Gold Benefits High deposition rates and efficient operation Nickel-free alternative with similar physical properties Antimicrobial and corrosion-resistant surface Functions as a barrier layer before gold plating Decorative and functional surface finish Compatible with brush and bath plating Real Gold Typical Parameters PropertyValue / RangeElectrolyte typeWhite bronze plating solutionMixing ratio1 part alkaline copper : 1 part White BronzeVoltage3.2–3.5 VTemperature18–25 °C (optimum ~22 °C)ElectrodeGraphite/platinumTypical alloy~42 % Cu / 58 % SnHardness450–500 HVDensity of deposit8.6–8.8 g/cm³Plating rate0.7–1.5 µm/minShelf life~4 weeks if stored correctlyStorage2–5 °C recommendedAir sensitiveYes — keep sealed Safety Information Follow all standard electroplating safety practices: Wear protective gloves, goggles, and clothing Avoid contact with skin and eyes Use in well-ventilated areas Keep out of reach of children Dispose of wastes per local regulations Conclusion The White Bronze Electrolyte SW10011.1 is a versatile plating solution that produces bright, antimicrobial white bronze coatings with mechanical and aesthetic properties close to nickel plating. It is especially useful where nickel use is restricted or undesirable, and as a barrier layer prior to gold plating in both decorative and functional applications.

Nickel Electrolyte BMG-091.1 High-Quality Nickel Electrolyte for Electroplating Metal Surfaces Short Description The Nickel Electrolyte BMG-091.1 is a ready-to-use galvanic solution for electroplating decorative nickel layers on metal parts. It is suitable for beginners, workshops, and professional applications. Nickel plating improves corrosion resistance, enhances surface finish, and prepares the surface for further coatings such as gold or chrome plating. real-gold.de What Is This Nickel Electrolyte Used For? This nickel electrolyte is designed for electroplating a smooth, bright nickel coating onto metal objects to: provide a protective layer against corrosion improve surface appearance and wear resistance act as an intermediate layer before gold, silver, or chrome plating real-gold.de Typical applications include: Automotive and machinery parts Decorative metal components Restoration and repair projects Hobby and craft electroplating How Does Nickel Plating Work? (Simple Explanation) Electroplating uses electric current to deposit metal from a liquid solution onto a workpiece. Clean and degrease the metal surface thoroughly. Attach the workpiece as the cathode (negative terminal). Immerse both the workpiece and a nickel anode in the nickel electrolyte. Apply direct current; nickel ions in the solution are reduced and form a solid nickel layer on the workpiece. real-gold.de Proper surface preparation and correct electrical settings are key to achieving a smooth, shiny nickel finish. Advantages of Nickel Electrolyte BMG-091.1 Easy to use for beginners and advanced users Produces uniform, bright nickel coatings Ideal as a protective layer or base for further plating processes Works with common plating methods such as tank plating, brush plating, and pen plating real-gold.de Technical Parameters PropertyValue / RangeNotesElectrolyte TypeNickel electrolyteFor decorative nickel platingWorking Temperature15–60 °CRoom temperature operation possibleVoltage (Tank Plating)~2–6.5 V~4 V recommendedVoltage (Pen / Brush Plating)~3–6 V~4.5 V recommendedCurrent Density0.5–4 A/dm²Up to ~7 A/dm² with bath movementpH Value~3.5–4.5Correctable with dilute acidDeposition Rate~1.3 µm/min at 3 A/dm²Typical plating performanceTypical SubstrateSteel, copper, brass, other metalsClean and prepare surfaceRecommended AnodesNickel or platinumBest results with appropriate anode selection Practical Application Notes Clean the workpiece meticulously before plating to ensure good adhesion. real-gold.de Nickel layers provide an excellent barrier layer for later gold, silver, or chrome plating. real-gold.de Slight movement of the electrolyte bath can help create a more uniform nickel layer. real-gold.de Nickel plating is widely used because nickel adheres well to many metals and provides a good base for further finishes. realgold-shop.de Safety Information Nickel electrolytes contain nickel compounds, which can cause allergic skin reactions and other health effects if mishandled: Wear protective gloves and eye protection Avoid skin and eye contact Work only in well-ventilated areas Do not inhale vapors or mists Keep out of reach of children Follow all instructions and the safety data sheet (SDS) real-gold.de Scope of Delivery Nickel Electrolyte BMG-091.1 Quantity according to selected size Important Notice This product is not a toy and requires basic electroplating knowledge. For best results, combine this electrolyte with proper pre-treatment and post-treatment products. Continuous monitoring of parameters such as voltage, current, and bath condition will improve plating quality

Graphite Electrode Ø 6 mm (BMG‑010) Short Description The Graphite Electrode Ø 6 mm (BMG‑010) is a durable, chemically inert electrode rod made from high‑density fine‑grain graphite. Designed for use as an anode or electrode in electroplating processes, it is ideal for bath, pen, and pad plating applications where a clean, metal‑free current supply is essential.  Product Description This graphite electrode is manufactured from highly compressed fine‑grain graphite, which dissolves only slowly in electrolytes. Unlike metallic anodes, graphite does not shed contaminating metal particles, ensuring cleaner coatings and higher deposit quality.  The 6 mm diameter rod, with an approximate length of 95 mm, fits standard plating fixtures, holders, and pen plating tools, making it easy to integrate into various electroplating setups Typical Applications Electroplating processes (e.g., silver, gold, copper, black nickel, chrome, white bronze) Pen, bath, and pad plating Activation and pre‑treatment steps Counter‑electrode or anode use in a wide range of electrolytes Situations where metal contamination must be avoided Key Benefits Chemically inert: prevents unwanted metal ion contamination in the plating bath. Versatile: compatible with most electroplating chemistries and techniques.  Slow wear: dissolves gradually, extending service life. Affordable: cost‑effective solution for frequent use.  Easy to use: fits common plating holders and pen plating tools. Material & Dimensions Material: High‑density fine‑grain graphite Diameter: 6 mm Length: approx. 95 mm (other lengths may be available)  Practical Tips Ensure electrodes are clean and free of oils before use.  Replace electrodes periodically as they slowly dissolve during electroplating. Graphite’s mild warming effect can help stabilize bath temperature during plating. Conclusion The Graphite Electrode Ø 6 mm is an effective and reliable anode/electrode for a wide range of electroplating applications. Its inert behavior, broad compatibility, and metal‑free current delivery make it a solid choice for hobbyists, workshops, labs, and professional plating operations.

Anode Fabric Pad Sleeve Fluffy BMG-015 – Uniform Coating & Maximum Control The Anode Fabric Pad Fluffy BMG-015 is a specially designed accessory for pen plating and tampon electroplating, ensuring consistent electrolyte distribution and controlled coating processes. Thanks to its fluffy, high-volume structure, the pad absorbs electrolyte efficiently and releases it evenly and continuously onto the surface. This results in clean, uniform and high-quality metal coatings, even in demanding applications. Key Benefits at a Glance Excellent electrolyte absorption and release Uniform liquid and current distribution Ideal for precise and controlled plating Suitable for: Pen plating Tampon plating Reduces streaking and uneven deposits Flexible and easy to replace Applications Selective metal plating Repair and touch-up work Fine detail applications Jewelry finishing Technical surface treatments Technical Parameters Product Type: Anode fabric pad (fluffy) Item Number: BMG-015 Material: High-absorbency textile fabric Structure: Fluffy / high-volume Function: Electrolyte carrier for anode applications Application Areas: Pen plating Tampon plating Electrolyte Absorption: Very high Electrolyte Release: Even and controlled Current Distribution: Supports uniform deposition Reusability: Limited (depending on application) Replacement: Quick and easy Application – Step by Step 1. Preparation Soak the fabric pad with the appropriate electrolyte Allow excess liquid to drip off slightly Attach to the anode or plating pen 2. Pen Plating Application Move the pad evenly across the surface Maintain consistent contact Control voltage and movement Ensures precise and clean results 3. Tampon Plating Application Use the pad as an electrolyte carrier Apply even pressure Maintain continuous motion  Ideal for selective plating applications Pro Tips for Best Results Replace pad regularly for consistent quality Avoid over-saturation → better control Uniform movement prevents streaks Always use clean electrolyte Conclusion The Anode Fabric Pad Fluffy BMG-015 is an essential accessory for achieving precise, uniform and high-quality results in pen and tampon electroplating. It ensures optimal control, clean finishes and significantly improved coating performance.