Covering pen

Betzmann Galvanik Pen Electroplating Pen - Product features at a glance: Our Galvanic Pen - Electroplating Pen consists of a graphite core that is ultimate for all coatings.       The pen for the finest and most delicate pen electroplating with graphite electrode. + 3 x felt tips + 2 x cable + alligator clip Suitable for plating most metals ideally suited for our BMG-25A and 50A electroplating systems.   The electroplating pens offer among others jewelers, watchmakers, jewelry manufacturers and also and also to all hobby electroplaters the possibility to galvanically refine pieces of jewelry in a simple way. The electroplating pens make it possible to carry out fine and very fine decorative electroplating work on jewelry and other small parts. In this way, jewelry can even be partially gold-plated. With the pen electroplating system it is possible to do a 2-tone precious metal coating even on very small surfaces. Whether in the studio, in the jewelry industry jewelers: the electroplating pens with the fine fiber pen attachments enable multifaceted color shades and sophisticated sophisticated results that will amaze you. The electroplating pens are also ideal for repair and touch-up work.  Electroplating Pens are ideally suited.   Directions for use: The plus cable is plugged in at the end of the grip piece, and a replaceable felt in the front. Please use one felt per electrolyte (they can be used for a very long time). The felts should be thoroughly soaked and moistened before use, as this is the only way they will pass the current.   The integrated graphite electrode is excellent for gold plating, chrome plating, silver plating, palladium plating, copper plating, zinc plating, black ruthenium, black chrome, black rhodium Nickel plating, rose gold, green gold, white gold and more.    Guide you will get when you buy the product.           

Graphite round rod - Graphite rod anode - Graphite electrode for gold plating.  Graphite electrodes are ultimate for all coatings. The advantage is that in some coatings with stainless steel electrodes, the dislodged metal parts disturb the coating. This does not happen with graphite electrodes, because graphite also filters out contaminated liquids. With bath electroplating, they also need to be replaced occasionally as they slowly dissolve during the plating process.   With pad electroplating, simply loosen the screw on the handle and replace with a new one.   Diameter 6 mm, length approx. 9 cm    Features Used for Doesn’t contaminate Cleaner Activating and electro-cleaning  Its resistive properties help to heat the solution you’re plating with Chromium plating, which needs to be plated at 25 degrees celsius; its natural heating action helps to maintain the solution’s optimal temperature Low cost Can be used for all plating processes but carbon electrodes deteriorate over a period of time and discolour swabs (discolouration does not affect the plating quality)    

PRODUCT PRESENTATION - GOLD ELECTROLYTE 999 FINE GOLD - 23,8 CARAT  WITH 4 GRAMS OF GOLD PER LITER   Do-it-yourself gold plating has never been so easy. Our Gold Electrolyte from Betzmann Galvanik can be purchased by anyone. Whether it is for use in highly professional laboratories, industry, luxury companies, to the use in the hobby, main or secondary trade, companies, schools, universities, TH , IHK or other authorities.   With this extremely fast and very hard depositing gold electrolyte from Betzmann Galvanik, you can usually coat the following metals directly: Stainless steel of all kinds, surgical steel, copper, silver, brass, nickel, iron, steel,     The pink color of the electrolyte is the hardness additive cobalt. This gives the otherwise much too soft gold an abrasion resistant surface. This is not toxic in the admixed composition.  The gold electrolyte from Betzmann Galvanik is anti-allergenic, was extracted from crisis- and conflict-free gold and is food-safe.    Our Betzmann Galvanik Gold Electrolyte has a very fast deposition and further achieves a very hard gold layer. It has a very good covering effect and is therefore one of the best products on the market worldwide. A special preservative results in a very long shelf life of at least 2 years and prevents sedimentation, which occurs with many other gold electrolytes.   The Gold Electrolyte from Betzmann Galvanik can be used for pen electroplating, pad electroplating and also for bath electroplating!    The Gold Electrolyte from Betzmann Galvanik is used worldwide, e.g. for the gold plating of boat parts made of brass that are exposed to salt water, medical technology, measurement technology, for optical gold plating, for technical gold plating, gold plating of drive shafts, musical instruments and their parts, both inside and outside, body jewelry, intimate protection, dental jewelry, dental technology, drills of all kinds, shisa, e-cigarettes so-called. Vaporizers, vehicle parts, engine parts, motorcycle parts, airplane interiors, exhaust systems and manifolds, as gold is very heat resistant, sporting goods, diving equipment, keys and pendants, jewelry, chains and rings of all kinds, piston rods, pipes, table feet, bathroom fixtures and many more.   Partial coatings are possible by masking and masking surrounding areas. To avoid material loss when coating sloping surfaces, we recommend our thickener/gel former. With this you can thicken all electrolytes also chrome remover, cleaner etc..     Also you can use with this gold mostly in the ratio 1:10 our mixer products like rose gold, white gold and green gold!   Optimal results are achieved with the platinum electrode 6mm - 10cm long or the flat platinum electrode, since platinum electrodes can build up very thick layers far above 10 microns and more. Graphite electrodes can also be used.  Gold content: 4 grams per liter    The procedure for gold plating: It is recommended to polish the surface to a shine first - the nicer the surface, the nicer the shine will be Thorough degreasing with the electrocleaner Activate the surface with the activator Gilding with platinum electrode starting around 5 volts     Operating Conditions and Deposit Data Plating Factor 0.01 A/cm2 Plating rate 0.12 micron per minute at 0.01A/cm2 Maximum plating thickness 4 microns Temperature 18 – 25 °C pH 4.4 – 5.0 Gold concentration 4 grams per litre Agitation Low Electrode Mesh or Platinum Rod Electrode Gold content in plate 99.9% (balance carbon) Cathode efficiency ~25% at Plating Factor = 0.01A/cm2 Hardness 190 – 210 Hv Density of deposit 19.3 g/cm3 Stress Medium Special storage requirements Away from sunlight Shelf life 1 – 2 years Health and Safety classification Harmful Special considerations Contains potassium cyanide (0.15%) Transport (UN number) None: Not classified as dangerous for transport      Signalword: Warning    H-phrases: H332 Harmful by inhalation. H312 Harmful in contact with skin. H302 Harmful if swallowed. EUH032 Contact with acids liberates very toxic gas. P phrases: P280 Wear protective gloves/protective clothing/eye protection/face protection. P301 IF INSPECTED:P310 Immediately call a POISON CENTER/doctor.