Black Nickel Electrolyte (Smoky Nickel) – Ready-to-Use Electrolyte for Tank, Pen and Brush PlatingProfessional Black Nickel Electrolyte for Decorative Dark Grey to Deep Black Nickel CoatingsThe Black Nickel Electrolyte (Smoky Nickel) from Betzmann Galvanik is a high-quality, ready-to-use plating solution designed for depositing decorative dark grey to deep black nickel coatings.The resulting coatings provide an elegant, modern appearance with a uniform colour finish and are widely used in the jewelry, watch, eyewear, design, restoration, and decorative metal finishing industries.Black Nickel is often used as a cost-effective alternative to Black Rhodium or Black Ruthenium. It offers an attractive dark metallic finish, good adhesion, and simple processing.The electrolyte is suitable for tank plating, pen plating, and brush/tampon plating, making it ideal for professional applications as well as repairs, prototypes, and small series production.Suitable Base MaterialsThe Black Nickel Electrolyte can be applied to various properly prepared metallic surfaces, including:NickelCopperBrassBronzeSilverGoldStainless steel (after suitable activation)Nickel-plated surfacesOther electroplated metalsFor optimum adhesion and durability, a suitable intermediate layer such as nickel or palladium may be recommended depending on the base material.Typical ApplicationsIdeal for:Jewelry manufacturingJewelry repairWatch casesWatch strapsEyewear framesWriting instrumentsDecorative metal componentsDesign objectsClassic restoration projectsModel makingCraftsElectroplating workshopsGoldsmithsJewelersProduct AdvantagesReady-to-use Black Nickel electrolyteDark grey to deep black finishElegant smoky nickel appearanceUniform coating formationGood adhesionDecorative final coatingEasy handlingSuitable for tank, pen and brush platingProfessional qualityIdeal for selective platingSuitable for single parts, repairs, and small production runsTechnical DataRecommended Operating ConditionsTank plating voltage: approx. 1.5–4.0 VoltsPen / brush plating voltage: approx. 3–6 VoltsBath temperature: 20–30 °CAnode material: Graphite electrode or Platinum electrodeReady-to-use electrolyteCoating PropertiesDark grey to deep black nickel coatingSatin to slightly glossy appearanceUniform colour distributionGood abrasion resistanceHigh colour stabilityDecorative final finishApplicationBefore plating, the workpiece must be thoroughly cleaned and activated to ensure optimum adhesion.For consistent results, voltage, electrode distance, plating time, and surface preparation should be adjusted according to the workpiece and application.The electrolyte is suitable for both small repair jobs and complete decorative coating of components.Supplied AsReady-to-use Black Nickel ElectrolyteAvailable in different container sizesQuality from Betzmann GalvanikBetzmann Galvanik supplies professional electrolytes for decorative and technical surface finishing applications.The Black Nickel Electrolyte (Smoky Nickel) produces elegant dark grey to deep black nickel surfaces with excellent colour uniformity and easy processing. It is the ideal solution for jewelry, watches, design objects, restoration projects, and decorative metal finishing – providing an attractive and economical alternative to Black Rhodium and Black Ruthenium coatings.

18K Rose Gold Electrolyte – Professional Rose Gold Plating Solution (4.0 g/L Au)Premium 18K Rose Gold Electrolyte for Brilliant Rose Gold and Red Gold PlatingThe 18K Rose Gold Electrolyte is a premium, ready-to-use rose gold plating solution designed for depositing elegant 18-karat rose gold and red gold coatings. This neutral gold electrolyte operates without free cyanide, features a stable pH value, and produces uniform, high-gloss, and highly adherent gold-copper alloy coatings.The balanced gold-copper alloy creates the characteristic warm rose gold color that is highly valued in jewelry manufacturing, luxury goods, and premium decorative finishing. The deposited coatings offer excellent hardness, outstanding wear resistance, and very good corrosion and tarnish resistance.With a gold content of 4.0 g/L Au and 3.0 g/L copper, the electrolyte produces brilliant rose gold coatings with thicknesses of up to 10 µm under optimum operating conditions.The electrolyte is suitable for both decorative and technical applications and can be used for tank plating, pen plating, and brush plating.ApplicationsThe 18K Rose Gold Electrolyte is ideal for:JewelryRingsNecklacesPendantsBraceletsEarringsWatches and watch componentsEyewear framesLuxury accessoriesDesigner productsDecorative metal finishingPremium surface finishingPrecision engineering componentsSuitable for:JewelersGoldsmithsJewelry manufacturersElectroplating companiesWatchmakersIndustrial applicationsProfessional workshopsProduct BenefitsReady-to-use 18K Rose Gold Electrolyte4.0 g/L Gold (Au)3.0 g/L Copper (Cu)Neutral electrolyteFree from free cyanideElegant warm rose gold finishBright, high-gloss coatingExcellent adhesionHigh hardnessOutstanding wear resistanceExcellent corrosion resistanceVery good tarnish resistanceCoating thickness up to 10 µmSuitable for decorative and technical applicationsCompatible with tank plating, pen plating, and brush platingProfessional electroplating qualitySuitable Base MaterialsThe electrolyte is suitable for a wide variety of metallic substrates and properly prepared electroplated surfaces.Suitable materials include:GoldSilverCopperBrassBronzeNickelPalladiumStainless steel (with appropriate pre-treatment)Suitable electroplated intermediate layersFor optimum adhesion and coating quality, all workpieces should be thoroughly cleaned, degreased, rinsed, and activated before plating.Technical SpecificationsProduct Type18K Rose Gold ElectrolyteGold Content4.0 g/L Au (3.5–4.5 g/L)Copper Content3.0 g/L Cu (2.5–3.5 g/L)pH Value7.5 (7.2–8.0)Density1.07 g/mlRecommended Operating ConditionsParameterValueVoltage1.6 Volts (1.4–1.8 V)Bath Temperature57 °C (55–60 °C)Electrode MaterialGraphite or Platinum ElectrodesAnode/Cathode RatioApprox. 2:1Workpiece AgitationRequiredCurrent DensityApprox. 0.3 A/dm² (0.1–0.5 A/dm²)Deposition RateApprox. 45 mg/A·minDeposition SpeedApprox. 0.1 µm/minBath FiltrationRecommended for bath volumes above 10 litersCoating PropertiesThe deposited gold-copper alloy provides:Elegant warm rose gold finishBrilliant high-gloss appearanceExcellent adhesionHigh hardnessOutstanding wear resistanceExcellent corrosion resistanceVery good tarnish resistanceUniform coating thicknessLong-lasting decorative finishDeposit CharacteristicsHardness: 380–400 HVMaximum Coating Thickness: Up to 10 µmTank Plating, Pen Plating or Brush Plating?The 18K Rose Gold Electrolyte is suitable for multiple electroplating methods.Tank PlatingIdeal for:Complete workpiecesBatch productionUniform coatingsHigher coating thicknessesPen PlatingIdeal for:RepairsSelective gold platingSmall surface areasTouch-up workBrush PlatingIdeal for:Large componentsLocalized platingFixed assembliesOn-site repairsProcessing RecommendationsFor optimum plating performance, all workpieces should be thoroughly cleaned, degreased, rinsed, and activated before electroplating. Maintaining the recommended operating parameters ensures uniform coating thickness, excellent adhesion, and a consistent rose gold color.Changes in voltage, temperature, or current density may influence the final color, coating thickness, and surface quality.Available VersionReady-to-Use 18K Rose Gold Electrolyte – 4.0 g/L AuQuality from Betzmann GalvanikBetzmann Galvanik develops premium precious metal electrolytes for professional electroplating applications in jewelry manufacturing, watchmaking, luxury goods, industrial finishing, and precision engineering.Our rose gold electrolytes are manufactured to the highest quality standards, ensuring excellent process stability, consistent plating performance, and brilliant 18K rose gold coatings with exceptional durability and premium appearance.

Gold Electrolyte BMG‑072 – High Speed Gold High-Quality High-Speed Gold Plating Electrolyte – 12 g Gold per Liter Short Description The Gold Electrolyte BMG‑072 (High Speed Gold) is a ready-to-use plating solution for fast and high-quality gold deposition on metal surfaces. With 12 grams of gold per liter, this electrolyte allows faster deposition, thicker layers in less time, and coverage of larger areas compared to lower-concentration gold baths. Its hard, uniform, and well-adhering gold layers make it suitable for hobbyists, workshops, labs, and professional industrial applications. Applications High Speed Gold Electrolyte is ideal for: Decorative gold plating (jewelry, pendants, trims) Technical gold plating (contact surfaces, circuit boards, measuring devices) Corrosion protection and durable surface finishing Multi-layer systems, e.g., Copper → Nickel → Gold Partial or full coverage of complex components The higher gold content allows faster results and higher deposition rates than standard gold baths. How it Works (Simple Explanation) Gold is deposited onto metal surfaces through direct current: Polish: Prepare a smooth, high-gloss surface. Clean: Thoroughly degrease (e.g., with an electrocleaner). Activate: Chemically activate the surface (e.g., with an activator). Gold Plating: Apply DC (approx. 4 V) with a platinum or graphite anode to deposit gold. Result: a hard, uniform gold layer with excellent gloss and high durability. Advantages High gold content (12 g/L) for faster deposition and thicker layers Very hard and uniform layers, even for prolonged plating Excellent coverage and adhesion on metals like stainless steel, copper, silver, brass, nickel, iron, and steel Suitable for tank, brush, and tampon plating Versatile for decorative and technical plating in hobby, industrial, or research applications Economical for larger surfaces or frequent use Technical Parameters PropertyValue / RangeElectrolyte typeGold plating solution (High Speed Gold)Gold contentapprox. 12 g/LOperating temperature14–25 °CVoltage range3.0–8.0 V (starting at ~4 V)Recommended anodePlatinum or graphiteGold content in depositapprox. 99.9 % (rest carbon)Deposition rateapprox. 0.7 µm/min at 3.5 V (Platinum anode)Layer hardnessapprox. 220–230 HVDeposit densityapprox. 19.0 g/cm³Voltage stressmediumStorageprotect from direct sunlightShelf life1–2 yearsHazard classHarmful / Irritant Note: Values are typical operational data; slight variations may occur depending on application. Application Instructions Surface preparation: Polish → Degrease → Activate Gold plating: Operate the electrolyte at ~4 V with a platinum or graphite anode Partial plating: Mask areas as needed (e.g., tape, nail polish) Sloped surfaces: Use a leveling agent or thickener to reduce material loss Safety Instructions Gold electrolytes contain chemicals and must be handled safely: Wear chemical-resistant gloves, safety glasses, and protective clothing Avoid contact with skin and eyes Rinse immediately with water if contact occurs Use only in well-ventilated areas Do not inhale vapors or aerosols Contains small amounts of potassium cyanide (~0.3%) – handle with care Do not ingest; keep out of reach of children Scope of Delivery Gold Electrolyte BMG‑072 – High Speed Gold Quantity according to selection Conclusion The Gold Electrolyte BMG‑072 (High Speed Gold) is a powerful, professional gold plating solution offering faster deposition rates and thicker layers than standard gold baths. It is ideal for decorative, technical, and industrial applications and adheres well to a broad range of metals, including stainless steel, brass, nickel, and steel. Its combination of high gold content, rapid deposition, and ease of use makes it perfect for hobbyists, workshops, and professionals seeking high-quality, durable, and shiny gold surfaces.

Alkaline Copper Electrolyte – Cyanide-Free Copper Bath for Acid-Sensitive MetalsProfessional Alkaline Copper Electrolyte for Tank, Pen and Brush PlatingThe Alkaline Copper Electrolyte from Betzmann Galvanik is a high-quality, cyanide-free copper electrolyte for the electroplating of acid-sensitive metals. It has been specially developed to reliably apply firmly adhering copper coatings on materials such as iron, steel, zinc and zinc die-cast alloys.Unlike acidic copper electrolytes, the alkaline copper electrolyte is ideally suited as an adhesion layer and intermediate coating for materials that may be attacked by acidic electrolytes.The electrolyte is suitable for both tank plating and pen/brush plating (tampon plating) and enables uniform, decorative and functional copper coatings at room temperature.Your AdvantagesCyanide-free alkaline copper electrolyteIdeal for acid-sensitive metalsExcellent adhesion on iron and steelVery good leveling propertiesGood throwing powerIntensive, attractive copper colourIdeal intermediate layer before bright copper platingSuitable for tank, pen and brush platingEasy application at room temperatureProfessional quality from Betzmann GalvanikWhy Use Alkaline Copper Plating?Many metals cannot be directly plated with an acidic copper electrolyte. Especially iron, steel and zinc require a special copper strike layer to achieve a permanently adherent copper coating.The alkaline copper electrolyte enables:Strongly adherent copper coatings on iron-based materialsProtection of sensitive base materialsPreparation for further electroplating processesConstruction of high-quality multilayer coating systemsAfter alkaline copper plating, the surface can be further processed with a bright acid copper electrolyte to achieve an especially smooth and glossy finish.Typical ApplicationsIdeal for:IronSteelZincZinc die-cast partsBrassBronzeCopperTinLeadMetal restorationClassic car partsModel makingJewellery manufacturingRepair workTechnical coatingsSuitable Base MaterialsSuitable for:✓ Lead✓ Bronze✓ Iron✓ Steel✓ Copper✓ Brass✓ Zinc✓ Zinc die-cast alloys✓ TinNot directly suitable for:✗ Aluminium✗ Chromium✗ TitaniumAluminium requires suitable pretreatment, for example with an aluminium activator.For unknown materials, a test coating should always be performed before application.Application InstructionsFor optimum results, workpieces must be thoroughly cleaned before copper plating.Remove:OilGreaseDirtOxide layersRustUse clean disposable gloves to prevent renewed contamination from skin oils.The alkaline copper electrolyte already works at room temperature and can be heated if required.The optimum operating temperature range is between 25 and 50 °C.Recommended Layer System for Perfect SurfacesA proven electroplating system:Base Material → Alkaline Copper → Bright Copper → Nickel → Gold / Chromium / Precious MetalsThe alkaline copper electrolyte provides excellent adhesion, while the bright copper electrolyte creates a smooth and highly reflective surface.Technical DataOperating DataCyanide-free alkaline copper electrolytepH value: 8–10Operating temperature: 20–60 °CWorking ConditionsCurrent density: 0.2–1.5 A/dm²Up to 3 A/dm² with solution movementTank Plating:Approx. 1.4 Volts (5 cm electrode distance)Approx. 1.5 Volts (10 cm electrode distance)Approx. 1.7 Volts (20 cm electrode distance)Pen and Brush Plating:2.5–6 VoltsRecommended: 4–5 VoltsAdditional parameters:Plating time: 10–45 minutesDeposition rate:approx. 0.4 µm/min at 1 A/dm² and 20 °CAnode material: Copper AnodeCoating PropertiesUniform copper coatingsExcellent adhesionVery good levelingGood throwing powerAttractive copper colourIdeal preparation for further electroplating processesSupplied AsReady-to-use alkaline copper electrolyteAvailable in various container sizesQuality from Betzmann GalvanikBetzmann Galvanik develops professional electrolytes for decorative and technical surface finishing. The Alkaline Copper Electrolyte is the ideal solution for safe and reliable copper plating of acid-sensitive metals such as iron, steel and zinc and provides the perfect foundation for high-quality multilayer electroplating systems.

Silver Electrolyte 30 g/L – Premium Silver Plating Solution for Tank, Pen & Brush PlatingProfessional Silver Electrolyte for Bright, Conductive and High-Quality Silver CoatingsThe Silver Electrolyte 30 g/L from Betzmann Galvanik is a premium, ready-to-use electroplating solution developed for depositing high-purity silver coatings on conductive metal surfaces. With a silver concentration of 30 grams per litre, this electrolyte provides fast deposition rates, brilliant finishes and outstanding electrical conductivity.The electrolyte is suitable for tank plating, pen plating and brush plating (swab plating), delivering professional results for both decorative and technical applications. Whether you are plating jewellery, electronic components, electrical contacts, cutlery or restoration projects, this silver plating solution produces uniform, highly adherent and durable silver deposits.Your Advantages at a Glance30 g of silver per litreReady-to-use professional electrolyteSuitable for tank plating, pen plating and brush platingBright, uniform silver depositsOutstanding electrical and thermal conductivityExcellent adhesionEven metal depositionSuitable for decorative and technical applicationsIdeal for hobbyists, workshops and industrial usersPremium quality from Betzmann GalvanikWhy Electroplate with Silver?Silver offers the highest electrical conductivity of all metals, combined with excellent thermal conductivity and an attractive bright white appearance. It is one of the most widely used precious metals in electroplating for both decorative and functional applications.Silver plating is commonly used for:Decorative finishesElectrical contactsPrinted circuit boards (PCBs)Connectors and terminalsJewelleryWatchesCutleryMusical instrumentsPrecision componentsRestoration workIn addition to its elegant appearance, a silver coating significantly improves conductivity while providing excellent wear resistance and protection against oxidation.Suitable Base MaterialsThe Silver Electrolyte is suitable for plating:CopperBrassBronzeNickelSteel (with appropriate pre-treatment)Stainless steel (after Nickel Strike activation)SilverCopper-plated componentsDepending on the substrate, we recommend using the appropriate activator or intermediate layer to achieve maximum adhesion.Recommended Plating StructureFor maximum durability and long-term colour stability, the following plating sequence is recommended:Base Material → Copper → Nickel → SilverThe nickel layer acts as a diffusion barrier, preventing copper migration into the silver coating and ensuring a bright, tarnish-resistant finish.Typical ApplicationsIdeal for:Jewellery manufacturingJewellery repairWatchmakingElectronicsPrinted circuit boards (PCBs)Electrical contactsConnectorsMusical instrumentsRestorationClassic carsModel makingLaboratoriesIndustrial electroplatingProfessional metal finishingApplicationBefore silver plating:Thoroughly clean and degrease the workpiece.Remove all oxide layers.Activate the surface according to the base material.During plating:For tank plating, immerse the workpiece completely in the electrolyte.For pen plating or brush plating, keep the electrode moving continuously across the surface to ensure uniform metal deposition.After plating, rinse the workpiece thoroughly with clean water and dry completely.Technical SpecificationsSilver concentration: 30 g/LOperating temperature: 15–30 °CpH value: Slightly acidic to neutralCurrent density: 0.5–3 A/dm²Tank plating voltage: Approx. 1.5–3.5 VPen & brush plating voltage: Approx. 3–7 VRecommended anodes: Platinum, graphite or silverCoating thickness: Approx. 1–5 µm (depending on plating time)Deposit purity: >99.9% silverThe above parameters are recommended values and may vary depending on workpiece geometry, electrode spacing and plating equipment.Safety InformationWear protective gloves and safety goggles.Avoid skin and eye contact.Use only in well-ventilated areas.Keep out of reach of children.Always follow the Safety Data Sheet (SDS).Quality from Betzmann GalvanikThe Silver Electrolyte 30 g/L from Betzmann Galvanik has been developed to meet the highest standards in modern electroplating. Its high silver concentration, excellent conductivity and easy handling make it ideal for decorative silver plating as well as demanding industrial applications. Combined with Betzmann Galvanik power supplies, electrodes and accessories, it delivers brilliant, durable and professional silver finishes every time.

Gold Electrolyte 8 g/L – 24K Hard Gold PlatingProfessional gold plating electrolyte containing 8 g of gold per liter for high-quality 24K gold deposits – suitable for tank plating, pen plating and tampon plating.This high-quality Gold Electrolyte 8 g/L is designed for producing uniform, durable and visually attractive 24-karat gold coatings. It can be used for conventional tank electroplating as well as for selective gold plating with a plating pen or tampon system.Ideal for jewelry, watches, metal components, restoration, repair work, model making, prototypes, individual pieces and professional surface finishing.Key Benefits8 g gold per liter24K gold / 99.9% goldSuitable for tank electroplatingSuitable for pen plating / brush platingSuitable for tampon plating / selective electroplatingHigh deposition performanceProduces uniform, high-quality gold depositsSuitable for professional applications and repair workAvailable in different container sizesTechnical support directly from Betzmann GalvanikTechnical DataParameterSpecificationGold content8 g/LGold purity99.9%Gold quality24KWorking voltageapprox. 3–5 VRecommended temperatureapprox. 14–25 °CDeposition rateapprox. 0.5 µm/min at 3.5 VMaximum recommended thicknessup to approx. 5 µmHardnessapprox. 220–230 HVSuitable anodePlatinum or carbonPlease note: Actual deposition rate and achievable coating thickness depend on the substrate, surface preparation, current density, temperature, electrolyte movement and plating time.Suitable for Tank, Pen and Tampon PlatingThis electrolyte offers excellent versatility for different gold-plating applications.With tank electroplating, complete components or assemblies can be coated with a uniform gold layer.For repairs, partial areas and difficult-to-reach surfaces, pen plating and tampon plating are particularly useful. These methods allow gold to be deposited selectively exactly where it is required, without immersing the entire component in a plating bath.Typical applications include:Gold plating repairsSelective gold platingJewelry and watchesElectrical contact areasMetal fittings and componentsIndividual partsRestoration workDecorative surface finishingPrototyping and small-batch productionCorrect Surface Preparation Is EssentialA high-quality gold coating always starts with proper surface preparation.The substrate must be thoroughly cleaned, degreased and properly activated before plating. Depending on the base material, an appropriate intermediate layer may also be required.Different substrates such as copper, brass, silver, stainless steel, steel, zinc alloys and aluminum require different preparation and activation procedures.For demanding applications, we recommend selecting the complete plating sequence according to the specific substrate and intended use.High-Quality 24K Gold DepositsWith an 8 g/L gold concentration, 24K gold and a hardness of approximately 220–230 HV, this electrolyte is suitable for producing attractive and relatively wear-resistant gold coatings.Depending on the application, thin decorative coatings or thicker functional gold layers can be deposited. For components exposed to mechanical wear, sufficient coating thickness is essential.Professional Gold Plating for Industry, Workshops and Individual ApplicationsWhether you are looking for a solution for complete tank plating or precise repair and selective plating with a pen or tampon, this 8 g/L Gold Electrolyte provides a versatile solution for professional gold plating applications.Betzmann Galvanik provides technical advice on electrolyte selection, surface preparation and the appropriate electroplating process for your application.Order Gold Electrolyte 8 g/LProfessional 24K Gold Electrolyte for tank plating, pen plating and tampon plating – ideal for gold plating, repair work, restoration and high-quality surface finishing.If you are unsure which preparation or intermediate layer is required for your particular substrate, please contact us for technical advice.